Product description and Application 產品描述和用途
ZSEJ90-2-N,ZSEJ90-2-M4 are two-step silane cross-linkable PE insulation compounds for low-voltage cables. They are mainly used for the insulation of low-voltage cables and control cables with working voltage for 3KV and below. The highest working temperature is 90℃.
ZSEJ90-2-N , ZSEJ90-2-M4 是低壓電線電纜用二步法硅烷交聯聚乙烯絕緣料。主要用于生產的低壓電力電纜和控制電纜的絕緣。電線電纜工作電壓為3KV及以下，最高工作溫度為90℃。
ZSEJ90-2-N is suitble for squeeze tube mold production process.
ZSEJ90-2-N 適用于擠管式生產模具
ZSEJ90-2-M4 is suitble for extrusion dies mold production process.
ZSEJ90-2-M4 適用于擠壓式生產模具
Above two models have the same physical and electrical properties, except different production molds.
二者只是電纜生產時模具不同，具有相同的物理和電氣性能
 
Processing Indicator 加工工藝  
Recommend to process with the PE extruder.  建議使用聚乙烯專用擠出機進行加工。

Model 牌號	Machine Barrel Temperature 機筒溫度	Molding Temprature 模頭溫度
ZSEJ90-2-N ZSEJ90-2-M4	155-175℃	180-190℃

 
Physical and Electrical Properties 物理和電氣性能

Item 試驗項目			Unit 單位	Technical requirements 技術要求
Density 密度			g/cm3	0.922±0.005
Tensile Strength 拉伸強度			MPa	≥13.5
Elongation at Break 斷裂伸長率			%	≥350
Brittle Temperature with Low Temperature 低溫脆化溫度			℃ 失效數	-76 ≤15/30
20℃Volume Resistivity 20℃體積電阻率			Ω·m	≥1.0×1014
20℃Dielectric Strength,50Hz 20℃介電強度, 50Hz			MV/m	≥25.0
20℃Dielectric Constant,50Hz 20℃介電常數, 50Hz			----	≤2.35
Air Aging Condition 熱空氣老化條件 135℃×168h		Tensile Strength Variation After Aging 拉伸強度變化率	%	±20
		Elongation Variation After Aging 斷裂伸長變化率	%	±20
Hot Set Test Condition 熱延伸試驗條件 1.0mm厚度×25℃環境溫度×65%環境濕度	48 hours later 48h后	Hot Elongation 負荷下伸長率	%	≤200
		Permanent Deformation after Cooling 冷卻后永久形變	%	≤50
	120 hours later 120h后	Hot Elongation 負荷下伸長率	%	≤160
		Permanent Deformation after Cooling 冷卻后永久形變	%	≤15
	240 hours later 240h后	Hot Elongation 負荷下伸長率	%	≤100
		Permanent Deformation after Cooling 冷卻后永久形變	%	≤5